Stainless Steel Flanges

Product Details:

Stainless Steel 317 is a modified version of Stainless Steel 316. It has high strength & corrosion resistance.

Stainless Steel 317 Chemical Composition

• Carbon; 0.080
• Phosphorus; 0.045
• Sulfur; 0.030
• Manganese; 2.00
• Silicon; 1.00
• Chromium; 19.0
• Molybdenum; 3.50
• Nickel; 13.0
• Iron; 61.0

Stainless Steel 317 Mechanical Properties
Tensile Strength(Mpa)psi; (620)89900
Yield Strength(Mpa)psi; (275)39900
Elongation(in 50mm); 45%
Hardness, Rockwell B ; 85

Product Details:

Stainless Steel 317L is a low carbon version of Stainless Steel 317. It has high strength & corrosion resistance. It produces stronger welds due to the low carbon content.

Stainless Steel 317L Chemical Composition
Carbon; 0.030
Sulfur; 0.030
Chromium; 18.0-20
Silicon; 1.00
Phosphorus; 0.045
Nickel; 11.0-15.0
Molybdenum; 3.0-4.0
Manganese; 2.00
Iron; Bal

Stainless Steel 317L Mechanical Properties
Tensile Strength(Mpa)psi; (595)86300
Yield Strength(Mpa)psi; (260)37700
Elongation(50mm) ; 55%
Hardness Rockwell B; 85

Product Details:

Stainless Steel 321 is advantageous for high temperature service because of its good mechanical properties. It offers higher creep & stress rupture properties than Stainless Steel 304.

Stainless Steel 321 Chemical Composition
Carbon; 0.08
Manganese; 2.00
Phosphorus; 0.045
Sulfur; 0.030
Silicon; 0.75
Chromium; 17.00-19.00
Nickel; 9.0-12.0
Molybdenum; 0.75
Copper; 0.75
Nitrogen; 0.75
Nickel; 0.10
Others; Ti=5x(C+N)min to 0.70max

Stainless Steel 321 Mechanical Properties
Tensile Strength, psi: 75,000 min
0.2% Offset Yield Strength, psi: 30,000
Elongation in 2" min: 40%

Product Details:

Aesteiron Steels LLP, provide premium quality of Stainless Steel 410 Flanges.

Stainless Steel 410 Chemical Composition

• Carbon; 0.15max
• Manganese; 1.00max
• Silicon; 1.00max
• Phosphorus; 0.040max
• Sulfur; 0.030max
• Chromium; 11.5-13.5
• Nickel; 0.75

Stainless Steel 410 Mechanical Properties
Tensile Strength (Mpa); 480min
0.2% Yield Strength(Mpa); 275min
Elongation(% in 50mm); 16min

Product Details:

Aesteiron Steels LLP, provides Stainless Steel 429 Flanges which is ferritic in nature. It provides good corrosion resistance & weldability.

Stainless Steel 429 Chemical Composition
Chromium; 14.0-16.0
Silicon; 1.00
Manganese; 1.00
Carbon; 0.12
Phosphorus; 0.040
Sulfur; 0.030
Iron; Bal

Stainless Steel 429 Mechanical Properties
Tensile Strength(Mpa)psi; (490)71068
0.2% Yield Strength(Mpa)psi; (310)44961
Elongation; 30%
Hardness Rockwell B; 88

Product Details:

Aesteiron Steels LLP, supplies high quality of Stainless Steel 420 Flanges.

Stainless Steel 420 Chemical Composition

• Carbon; 0.15min
• Manganese; 1.00max
• Silicon; 1.00max
• Phosphorus; 0.040max
• Sulfur; 0.030max
• Chromium; 12.0-14.0

Stainless Steel 420 Mechanical Properties
Tensile Strength(Mpa); 655
0.2% Proof Strength(Mpa); 345
Elongation(% 50mm); 25%

Product Details:

SS 416 is a free machining stainless with a machinability of 85% highest of all stainless steels.

Stainless Steel 416 Chemical Composition
Carbon; 0.15max
Manganese; 1.25max
Silicon; 1.00max
Phosphorus; 0.060max
Sulfur; 0.15max
Chromium; 12.0-14.0
Molybdenum; 0.60max

Stainless Steel 416 Mechanical Properties
Tensile Strength(Mpa); 517
0.2% Yield Strength(Mpa); 275
Elongation(% in 50mm); 30
Hardness Brinell(HB); 262

Product Details:

Aesteiron Steels LLP, is one of the leading manufacturers & suppliers of Stainless Steel 301 Flanges.

Standards:
SS 301
AFNOR Z 12 CN 17-07
WNR 1.4310
UNI X 12 CrNi 1707
JIS SUS 301
UNS S30100
UNE X 12 CrNi 17-07
SIS 23 31
BSI 301S21
EURONORM X 12 CrNi 17 7
ASTM A182 Gr 301 Flanges

We are:
SS 301 Flanges Stockist
Z 12 CN 17-07 Flanges Stockist
1.4310 Flanges Stockist
X 12 CrNi 1707 Flanges Stockist
SUS 301 Flanges Stockist
X 12 CrNi 17-07 Flanges Stockist
23 31 Flanges Stockist
BSI 301S21 Flanges Stockist
X 12 CrNi 17 7 Flanges Stockist
S30100 Flanges Stockist
ASTM A182 Gr 301 Flanges Stockist
SS 301 Flanges Suppliers
Z 12 CN 17-07 Flanges Suppliers
1.4310 Flanges Suppliers
X 12 CrNi 1707 Flanges Suppliers
SUS 301 Flanges Suppliers
X 12 CrNi 17-07 Flanges Suppliers
23 31 Flanges Suppliers
BSI 301S21 Flanges Suppliers
X 12 CrNi 17 7 Flanges Suppliers
S30100 Flanges Suppliers
ASTM A182 Gr 301 Flanges Suppliers
SS 301 Flanges Traders
Z 12 CN 17-07 Flanges Traders
1.4310 Sheets Flanges Traders
X 12 CrNi 1707 Flanges Traders
SUS 301 Flanges Traders
X 12 CrNi 17-07 Flanges Traders
23 31 Flanges Traders
BSI 301S21 Flanges Traders
X 12 CrNi 17 7 Flanges Traders
S30100 Flanges Traders
ASTM A182 Gr 301 Flanges Traders
SS 301 Flanges Dealers
Z 12 CN 17-07 Flanges Dealers
1.4310 Flanges Dealers
X 12 CrNi 1707 Flanges Dealers
SUS 301 Flanges Dealers
X 12 CrNi 17-07 Flanges Dealers
23 31 Flanges Dealers
BSI 301S21 Flanges Dealers
X 12 CrNi 17 7 Flanges Dealers
S30100 Flanges Dealers
ASTM A182 Gr 301 Flanges Dealers
SS 301 Flanges Manufacturers
Z 12 CN 17-07 Flanges Manufacturers
1.4310 Flanges Manufacturers
X 12 CrNi 1707 Flanges Manufacturers
SUS 301 Flanges Manufacturers
X 12 CrNi 17-07 Flanges Manufacturers
23 31 Flanges Manufacturers
BSI 301S21 Flanges Manufacturers
X 12 CrNi 17 7 Flanges Manufacturers
S30100 Flanges Manufacturers
ASTM A182 Gr 301 Flanges Manufacturers
SS 301 Flanges Exporters
Z 12 CN 17-07 Flanges Exporters
1.4310 Flanges Exporters
X 12 CrNi 1707 Flanges Exporters
SUS 301 Flanges Exporters
X 12 CrNi 17-07 Flanges Exporters
23 31 Flanges Exporters
BSI 301S21 Flanges Exporters
X 12 CrNi 17 7 Flanges Exporters
S30100 Flanges Exporters
ASTM A182 Gr 301 Flanges Exporters

Stainless Steel 301 Chemical Composition
Carbon: 0.15max
Manganese: 2max
Phosphorus: 0.045max
Sulfur: 0.03max
Silicon: 1max
Chromium: 16.0-18.0
Nickel: 6.0-8.0
Nitrogen: 0.1max

Stainless Steel 301 Mechanical Properties
Tensile Strength, min: 75ksi
Yield Strength, min: 30ksi
Elongation, min: 40%
Hardness: 95HRB

Please contact us for more details.

Product Details:

Stainless Steel 305 is an austenitic chromium nickel stainless steel with a low rate of work hardening. This low rate of work hardening makes its suitable for many deep drawing applications.

Stainless Steel 305 Chemical Composition

Stainless Steel 305 Mechanical Properties

Product Details:

Stainless Steel 310S is an austenitic stainless steel that combines excellent high temperature properties with good ductility & weldability.

Stainless Steel 310S Chemical Composition

Stainless Steel 310S Mechanical Properties

Product Details:

Stainless Steel 314 has excellent high temperature resistance characteristics among the chromium nickel steel.

Stainless Steel 314 Chemical Composition

Stainless Steel 314 Mechanical Properties

Product Details:

Stainless Steel 316 is an austenitic chromium nickel stainless steel containing molybdenum. Its typical uses are heat exchangers, jet engine parts, pharmaceuticals, chemical equipments etc.

Stainless Steel 316 Chemical Composition
Carbon; 0.08max
Manganese; 2.00max
Phosphorus; 0.045max
Sulfur; 0.030max
Silicon; 0.75max
Chromium; 16.0-18.0
Nickel; 10.0-14.0
Molybdenum; 2.0-3.0
Nitrogen; 0.10max
Iron; Bal

Stainless Steel 316 Mechanical Properties
Ultimate Tensile Strength ksi(Mpa); 84(579)
0.2% Yield Strength ksi(Mpa); 42(290)
Elongation % in 2" (50.8mm); 50
Hardness Rockwell; B79

Product Details:

Stainless Steel 316H has greater tensile yield strength, has greater long & short term creep strength & greater tensile yield strength.

Stainless Steel 316H Chemical Composition

• Carbon; 0.04-0.10
• Silicon; 0.75
• Manganese; 2.00
• Phosphorus; 0.045
• Sulfur; 0.030
• Chromium; 16.0-18.0
• Molybdenum; 2.00-3.00
• Nickel; 10.0-14.0

Stainless Steel 316H Mechanical Properties
0.2% Proof Stress(Mpa); 205
Tensile Strength(Mpa); 515
Elongation; 40%
Hardness HB; 217max

Product Details:

Stainless Steel 316L provides higher creep, stress to rupture & tensile strength at elevated temperature.

Stainless Steel 316L Chemical Composition

• Carbon; 0.03max
• Manganese; 2.00max
• Silicon; 0.75max
• Phosphorus; 0.045max
• Sulfur; 0.030max
• Chromium; 16.0-18.0
• Molybdenum; 2.0-3.0
• Nickel; 10.0-14.0
• Nitrogen; 0.10max

Stainless Steel 316L Mechanical Properties
Tensile Strength(Mpa); 485min
0.2% Yield Strength(Mpa); 170min
Elongation(% in 50mm); 40min
Hardness Rockwell B; 95max

Product Details:

Stainless Steel 316N is mainly used in furance parts, heat exchangers, jet engine parts & pharmaceuticals tanks etc.

Stainless Steel 316N Chemical Composition

• Carbon; 0.08
• Manganese; 2.00
• Phosphorus; 0.045
• Sulfur; 0.030
• Silicon; 0.75
• Chromium; 16.0-18.0
• Nitrogen; 10.0-14.0
• Molybdenum; 2.0-3.0
• Nickel; 0.1-0.16

Stainless Steel 316N Mechanical Properties
Tensile Strength(Mpa); 550
Yield Strength (Mpa); 240
Elongation in 2in or 50mm; 35%
Hardness Rockwell B; 95

Product Details:

Stainless Steel 321H is similar to 304 but with higher content & stabilized with titanium. It has good welding characteristics & post welding is not normally required to restore its excellent performance in a wide range of corrosive conditions.

Stainless Steel 321H Chemical Composition

• Chromium; 17.0-19.0
• Manganese; 2.00max
• Silicon; 0.75max
• Nickel; 9.0-12.0
• Phosphorus; 0.045max
• Sulfur; 0.030max
• Carbon; 0.080max
• Nitrogen; 0.1max
• Titanium; 5(C+N)-0.700

Stainless Steel 321H Mechanical Properties
Yield Strength, ksi: 30
Tensile Strength, ksi: 75
Elongation; 40%
Hardness; 95

Product Details:

Stainless Steel 347 provides good corrosion resistance. It is useful to make rocket engines parts, aircraft collector rings & chemical production equipments.

Stainless Steel 347 Chemical Composition
Nickel; 11.00
Chromium; 18.0
Iron; bal
Silicon; 1.00
Manganese; 2.00
Carbon; 0.080
Phosphorus; 0.045
Sulfur; 0.030
Cb+Ta; 10XC

Stainless Steel 347 Mechanical Properties
0.2% Offset Yield Strength psi(Mpa); 30,000(205)
Ultimate Tensile Strength psi(Mpa); 75,000(515)
Elongation; 40%min

Product Details:

Aesteiron Steels LLP, is engaged in manufacturing and supplying an optimal quality range of Stainless Steel 430F Flanges.

Stainless Steel 430F Chemical Composition

• Carbon; 0.12max
• Chromium; 16.0-18.0
• Manganese; 1.25max
• Molybdenum; 0.6max
• Phosphorus; 0.06max
• Silicon; 1.00max
• Sulfur; 0.15min
• Iron; Bal

 

Product Details:

Aesteiron Steels LLP, is engaged in manufacturing and supplying an optimal quality range of Stainless Steel 430Ti Flanges.

Stainless Steel 430Ti Chemical Composition
Carbon; 0.10
Phosphorus; 0.040
Sulfur; 0.030
Chromium; 16.0-19.5
Manganese; 1.00max
Silicon; 1.00max
Nickel; 0.8
Titanium; 0.50min
Iron; 76.0-80.0

Stainless Steel 430Ti Mechanical Properties
Tensile Strength(Mpa)psi; (515)74695
Yield Strength(Mpa)psi; (310)44962
Elongation; 30%

Product Details:

Stainless Steel 303 Se offers excellent machinability, good strength & corrosion resistance. This stainless steel is commonly used in parts requiring cold forming after machining.

Stainless Steel 303 Se Chemical Composition

Stainless Steel 303 Se Mechanical Properties

Product Details:

Stainless Steel 330 is an austenitic, nickel chromium iron silicon alloy. It has excellent resistence to carburization & oxidation. It is used in a variety of furance components as well as in gas turbine, heat exchangers, general heat treating equipments.

Stainless Steel 330 Chemical Composition

• Carbon; 0.08max
• Chromium; 17.0-20.0
• Copper; 1.00max
• Iron; Bal
• Lead; 0.005max
• Manganese; 2.00max
• Nickel; 34.0-37.0
• Phosphorus; 0.030max
• Silicon; 0.75-1.50
• Sulphur; 0.030max
• Tin; 0.025max

Stainless Steel 330 Mechanical Properties
Tensile Strength, ksi(min); 70
0.2% Offset Yield Strength, ksi(min); 30
Elongation; 30%min
Hardness Rockwell B; 90

Product Details:

Stainless Steel 329 is a duplex stainless steel with improved machinability. It has very good corrosion resistance particulary in chloride bearing environments.

Stainless Steel 329 Chemical Composition

• Carbon; 0.08max
• Iron; Bal
• Manganese; 1.00max
• Silicon; 0.75max
• Sulfur; 0.030max
• Phosphorus; 0.040max
• Chromium; 23.0-28.0
• Nickel; 2.5-5.0
• Molybdenum; 1.0-2.0

Stainless Steel 329 Mechanical Properties
Tensile Strength (Mpa)psi; (725)10500
Yield Strength (Mpa)psi; (550)79800
Elongation 2" min; 25%

Product Details:

Aesteiron Steels LLP, provides Stainless Steel 405 flanges which is used in quenching racks, annealing boxes, partitions, steam nozzels.

Stainless Steel 405 Chemical Composition

Stainless Steel 405 Mechanical Properties

Product Details:

Aesteiron Steels LLP, provides 403 Stainless Steel which is used in turbine parts & compressor blades. Stainless Steel are high alloy steels with good corrosion resistance due to the presence of large amounts of chromium in these steels.

Stainless Steel 403 Chemical Composition
Carbon; 0.15
Phosphorus; 0.040
Sulfur; 0.030
Manganese; 1.00
Silicon; 0.50
Iron; 86

Stainless Steel 403 Mechanical Properties
Tensile Strength(Mpa)psi; (485)70300
Yield Strength(Mpa)psi; (310)45000
Elongation; 25%

Product Details:

Aesteiron Steels LLP, provides premium of Stainless Steel 304Cu Flanges.


Stainless Steel 304Cu Chemical Composition

Stainless Steel 304Cu Mechanical Properties

Product Details:

Stainless Steel 304N provdes good corrosion resistance than grade 302 & it is non magnetic in nature. However its non maganetic in nature when cold worked acquires a slightly magnetic quality.

Stainless Steel 304N Chemical Composition

Stainless Steel 304N Mechanical Properties

Product Details:

Stainless Steel 310 combines excellent high temperature properties with good ductility & weldability, is designed for high temperature service.

Stainless Steel 310 Chemical Composition

Stainless Steel 310 Mechanical Properties

Product Details:

Stainless Steel 316F provides high creep strength at high temperature & good heat resistance. SS 316F is used for surgical implants, food & pharmaceutical processing & industrial equipment.

Stainless Steel 316F Chemical Composition

• Carbon; 0.08
• Phosphorus; 0.020
• Sulfur; 0.10min
• Manganese; 2.00
• Chromium; 16.0-18.0
• Nickel; 10.0-14.0
• Molybdenum; 1.75-2.50
• Silicon; 1.00
• Iron; Bal

Stainless Steel 316F Mechanical Properties
Tensile Strength(Mpa)psi; (585)84800
Yield Strength(Mpa)psi; (260)37700
Elongation (in 50mm); 60%
Hardness, Rockwell B; 85

Product Details:

Aesteiron has gained an honour in the field of offering 304 Stainless Steel Flanges to the clients. 304 Stainless Steel Flanges are designed with care using current techniques under the visionary guidance of accomplished professionals at manufacturing unit. Offered range is stringently tested on various parameters of quality for ensuring flawlessness and defect free. These products are widely used in various industries and widely appreciated by clients for owning unmatchable characteristics. Offered range supplied in quality assured packaging material. It has very good drawability. It exhibit excellent resistence to a wide range of atmospheric, chemical, textile, petroleum & food industry.

Stainless Steel 304 Chemical Composition

Stainless Steel 304 Mechanical Properties

Product Details:

Aesteiron Steels LLP, is one of the leading manufacturers & suppliers of Stainless Steel 302 Flanges.

Standards:
SS 302
AFNOR Z 10 CN 18-09

DIN X 5 CrNi 18 7

WNR 1.4319

UNS S30200

UNI X 10 CrNi 1809

JIS SUS 302

UNE X 10 CrNi 18-09

SIS 23 31

BSI 302S25

EURONORM X 10 CrNi 18 9

ASTM A182 Gr. 302 Flanges

 

We are:

SS 302 Flanges Stockist
Z 10 CN 18-09 Flanges Stockist

X 5 CrNi 18 7 Flanges Stockist

1.4319 Flanges Stockist

S30200 Flanges Stockist

X 10 CrNi 1809 Flanges Stockist

SUS 302 Flanges Stockist

X 10 CrNi 18-09 Flanges Stockist

23 31 Flanges Stockist

302S25 Flanges Stockist

X 10 CrNi 18 9 Flanges Stockist

ASTM A182 Gr. 302 Flanges Stockist

SS 302 Flanges Suppliers
Z 10 CN 18-09 Flanges Suppliers

X 5 CrNi 18 7 Flanges Suppliers

1.4319 Flanges Suppliers

S30200 Flanges Suppliers

X 10 CrNi 1809 Flanges Suppliers

SUS 302 Flanges Suppliers

X 10 CrNi 18-09 Flanges Suppliers

23 31 Flanges Suppliers

302S25 Flanges Suppliers

X 10 CrNi 18 9 Flanges Suppliers

ASTM A182 Gr. 302 Flanges Suppliers

SS 302 Flanges Traders
Z 10 CN 18-09 Flanges Traders

X 5 CrNi 18 7 Flanges Traders

1.4319 Flanges Traders

S30200 Flanges Traders

X 10 CrNi 1809 Flanges Traders

SUS 302 Flanges Traders

X 10 CrNi 18-09 Flanges Traders

23 31 Flanges Traders

302S25 Flanges Traders

X 10 CrNi 18 9 Flanges Traders

ASTM A182 Gr. 302 Flanges Traders

SS 302 Flanges Dealers
Z 10 CN 18-09 Flanges Dealers

X 5 CrNi 18 7 Flanges Dealers

1.4319 Flanges Dealers

S30200 Flanges Dealers

X 10 CrNi 1809 Flanges Dealers

SUS 302 Flanges Dealers

X 10 CrNi 18-09 Flanges Dealers

23 31 Flanges Dealers

302S25 Flanges Dealers

X 10 CrNi 18 9 Flanges Dealers

ASTM A182 Gr. 302 Flanges Dealers

SS 302 Flanges Exporters
Z 10 CN 18-09 Flanges Exporters

X 5 CrNi 18 7 Flanges Exporters

1.4319 Flanges Exporters

S30200 Flanges Exporters

X 10 CrNi 1809 Flanges Exporters

SUS 302 Flanges Exporters

X 10 CrNi 18-09 Flanges Exporters

23 31 Flanges Exporters

302S25 Flanges Exporters

X 10 CrNi 18 9 Flanges Exporters

ASTM A182 Gr. 302 Flanges Exporters

SS 302 Flanges Manufacturers
Z 10 CN 18-09 Flanges Manufacturers

X 5 CrNi 18 7 Flanges Manufacturers

1.4319 Flanges Manufacturers

S30200 Flanges Manufacturers

X 10 CrNi 1809 Flanges Manufacturers

SUS 302 Flanges Manufacturers

X 10 CrNi 18-09 Flanges Manufacturers

23 31 Flanges Manufacturers

302S25 Flanges Manufacturers

X 10 CrNi 18 9 Flanges Manufacturers

ASTM A182 Gr. 302 Flanges Manufacturers

 

Chemical Composition

C: 0.15max

Mn: 2.00max

P: 0.045max

S: 0.030max

Si: 1.00max

Cr: 17.0-19.0

Ni: 8.0-10.0

N: 0.10max

 

Mechanical Properties

Tensile Strength ksi(MPa): 90(620)

Yield Strength ksi(MPa): 40(275)

Elongation%: 60

 

 

Please contact us for more details.

 

 

Additional Information:

• Packaging Details: Shrink Wrapping, Jute Wrapping, Wooden Boxes etc