Nickel

Product Details:

ASTM B162 Nickel 200, is used for food processing equipment, marine & offshore engineering, salt production, manufacture & handling of sodium hydroxide, particularly at temperature above 300°F.

ASTM B162 Nickel 200 Chemical Composition
Carbon; 0.15max
Manganese; 0.35max
Sulfur; 0.01max
Silicon; 0.35max
Copper; 0.25max
Nickel; 99.0min
Iron; 0.40max

ASTM B162 Nickel 200 Mechanical Properties
Tensile Strength; 55-80ksi
0.2% Yield Strength; 15-40ksi
Elongation; 40-60%

Product Details:

ASTM B161 Nickel 201 Sheet, Strip has good mehanical properties & excellent resistance to many corrosive environment. Other useful features of the alloy are its magnetic properties, high thermal & electrical conductivities, low gas content & low vapour pressure

ASTM B161 Nickel 201 Chemical Composition
Carbon; 0.15max
Manganese; 0.35max
Silicon; 0.35max
Sulfur; 0.01max
Nickel+Cobalt; 99.0min
Copper; 0.25max
Iron; 0.40max

ASTM B161 Nickel 201 Mechanical Properties
Tensile Strength,min; 50ksi
0.2% Offset Yield Strength; 10ksi
Elongation; 40%min

Product Details:

Owing to the efforts of our competent professionals, we have been constantly involved in manufacturing, exporting and supplying a qualitative assortment of Nickel Alloy Sheet. We offer this sheet in various shapes and sizes, in order to meet the various requirements of clients. Apart from this, this sheet is designed using the best quality raw material and latest technology in compliance with global industrial norms.

Nickel alloys sheets coils are available in the following grades:-

Nickel 200/ Nickel 201: UNS N02200, N02201, ASTM-B-160, ASTM B162, ASTM B622
Nickel 400: N04400, AMS 4544, AMS 4574, AMS 4575, AMS 4576, AMS 4674, AMS 4675, AMS 4730, ASTM-B-164, QQ-N-281 A, QQ-N-281 B
Nickel 405: AMS 4544, AMS 4574, AMS 4575, AMS 4576, AMS 4674, AMS 4675, AMS 4730, QQ-N-281 A, QQ-N-281 B
Nickel K-500: N05500, AMS 4544, AMS 4574, AMS 4575, AMS 4576, AMS 4674, AMS 4675, AMS 4730, ASTM-B-865, QQ-N-281 A, QQ-N-281 B

Nickel Sheets Features:

• Ultra thin sheets
• No risk of corrosion
• No abrasion problems
• Scratch resistant surface
• Reflective surface shine
• Convenient to carry

Product Details:

ASTM B163 Nickel 201, is highly resistant to various chemicals, excellent resistance to caustic alkalies, high electrical conductivity, excellent corrosion resistance to distilled & natural waters.

ASTM B163 Nickel 201 Chemical Composition

• Carbon; 0.02max
• Manganese; 0.35max
• Copper; 0.25max
• Sulfur; 0.01max
• Silicon; 0.35maxNickel; 99.0min
• Iron; 0.40max

ASTM B163 Nickel 201 Mechanical Properties
Tensile Strength; 55-75ksi
0.2% Yield Strength; 12-30ksi
Elongation; 60-40%
Hardness; 70max

Product Details:

ASTM B723 Nickel 201, has good resistance to corrosion in acids & alkalis & is most useful under reducing conditions. It is outstanding to caustic alkalis upto & including the molten state.

Chemical Composition
Carbon; 0.2max
Manganese; 0.35max
Copper; 0.25max
Sulfur; 0.1max
Silicon; 0.35max
Nickel; 99.0min
Iron; 0.40max

Mechanical Properties
Tensile Strength; 50ksi min(345Mpa min)
0.2% Offset Yield Strength; 12ksi min(83Mpa min)
Elongation; 30-35%

Product Details:

ASTM B366 Nickel 200 Pipe Fittings, provides high thermal & electrical conductivity in comparison to nickel base alloy, stainless & low alloy steel.

ASTM B366 Nickel 200 Chemical Composition

• Carbon; 0.15max
• Manganese; 0.35max
• Silicon; 0.35max
• Sulfur; 0.010max
• Iron; 0.40max
• Copper; 0.25max
• Nickel+Cobalt; 99.0min

ASTM B366 Nickel 200 Mechanical Properties
Tensile Strength; 55ksi min(380Mpa min)
0.2% Offset Yield Strength; 15ksi min(100Mpa min)
Elongation; 35-40%

Product Details:

ASTM B161 Nickel 201 Pipe, is used for chemical processing & storage, synthetic fiber production, food processing, processess where sodium hydroxide is used.

Chemical Composition
Carbon; 0.15max
Manganese; 0.35max
Copper; 0.25max
Silicon; 0.35max
Sulfur; 0.01max
Iron; 0.40max
Nickel; 99.0min

Mechanical Properties
Tensile Strength(min); 50ksi, 345Mpa
0.2% Yield Strength; 10ksi, 70Mpa
Elongation; 40%min

Product Details:

ASTM B127 Nickel 200, is highly resistant to various reducing chemicals. It has excellent resistance to caustic alkalies. It also has corrosion resistance to distilled & natural waters.

Chemical Composition
Nickel; 99.0min
Iron; 0.40max
Copper; 0.25max
Carbon; 0.15max
Manganese; 0.35max
Sulfur; 0.01max
Silicon; 0.35max

Mechanical Properties
Tensile Strength; 55ksi min(380Mpa min)
0.2% Offset Yield Strength; 15ksi min(100Mpa min)
Elongation; 35-40%

Product Details:

ASTM F3 Nickel 205, is a wrought nickel alloy having controlled additions of small amounts of magnesium & titanium. It exhibits an excellent combination of mechanical, electrical & corrosion resistant properties. It also has good oxidation resistance.

ASTM F3 Nickel 205 Chemical Composition
Nickel+Cobalt; 99.00min
Magnesium; 0.01-0.08
Titanium; 0.01-0.05
Copper; 0.15max
Iron; 0.20max
Carbon; 0.15max
Silicon; 0.15max
Sulfur; 0.008max
Manganese; 0.35max

ASTM F3 Nickel 205 Mechanical Properties
Tensile Strength; 58-73ksi(400-500Mpa)
0.2% Offset Yield Strength; 60ksi(414Mpa)

Product Details:

ASTM B163 Nickel 200 is especially useful to those who are looking to maintain the purity of their products. This includes food handling, caustic alkalis, manufacturing of synthetic fibers & structural application that demand corrosion resistance.

ASTM B163 Nickel 200 Chemical Composition
Nickel; 99.0min
Iron; 0.40max
Copper; 0.25max
Carbon; 0.15max
Manganese; 0.35max
Sulfur; 0.01max
Silicon; 0.35max

ASTM B163 Nickel 200 Mechanical Properties
Tensile Strength; 55-75ksi
0.2% Yield Strength; 12-30ksi
Elongation; 40-60%
Hardness(HRB); 70max

Product Details:

Aesteiron Steels LLP, is the leading suppliers of ASTM F290 Nickel 211 Wire.

ASTM F290 Nickel 211 Chemical Composition
Carbon; 0.2max
Copper; 0.25max
Iron; 0.75max
Manganese; 4.25-5.25
Nickel; Bal
Silicon; 0.15max
Sulphur; 0.015max

ASTM F290 Nickel 211 Mechanical Properties
Tensile Strength; 650-800Mpa
Yield Strength; 350-550Mpa
Elongation; 8-25%

Product Details:

ASTM B725 Nickel 200, provides highly ductile mechanical properties across a wide temperature range. It provides highly ductile mechanical properties across a wide temperature range.

ASTM B725 Nickel 200 Chemical Composition
Carbon; 0.15max
Manganese; 0.35max
Silicon; 0.35max
Sulfur; 0.010max
Iron; 0.40max
Copper; 0.25max
Nickel+Cobalt; 99.00min

ASTM B725 Nickel 200 Mechanical Properties
Tensile Strength; 55ksi min(380Mpa min)
0.2% Offset Yield Strength; 15ksi min(100Mpa min)
Elongation; 35-40%

Product Details:

ASTM F290 Nickel 233, is a commercially pure wrought nickel alloy that exhibits excellent corrosion resistance & high electrical & thermal conductivities.

ASTM F290 Nickel 233 Chemical Composition
Carbon; 0.1max
Mangnesium; 0.01-0.10
Manganese; 0.3max
Silicon; 0.1max
Iron; 0.1max
Copper; 0.1max
Sulfur; 0.008max
Titanium; 0.005max
Nickel; Bal

ASTM F290 Nickel 233 Mechanical Properties
Tensile Strength; 650-880Mpa, 94275-127633psi
Yield Strength; 350-550Mpa, 50763-79771psi
Elongation; 8-25%

Product Details:

ASTM B729 Nickel 200, is useful for food processing equipment, electrical & electronic parts, aerospace components, rocket motor casing & transducers.

Chemical Composition
Nickel; 99.0min
Iron; 0.40max
Copper; 0.25max
Carbon; 0.15max
Manganese; 0.35max
Sulfur; 0.1max
Silicon; 0.35max

Mechanical Properties
Ultimate Tensile Strength, psi; 72,000
0.2% Offset Yield Strength, psi; 25,000
Elongation in 2" ; 40%
Hardness Rockwell; B61

Product Details:

ASTM F3 Nickel 270, has low base hardness & high ductility. It is useful for electrical resistance thermometers, platters bars, passive cathode, fluorescent lamp components & electrolytic cell anodes.

ASTM F3 Nickel 270 Chemical Composition
Nickel+Cobalt; 99.9min
Copper; 0.01max
Iron; 0.05max
Manganese; 0.003max
Carbon; 0.02max
Sulfur; 0.003max
Titanium; 0.005max
Manganese; 0.005max
Silicon; 0.005max

ASTM F3 Nickel 270 Mechanical Properties
Tensile Strength; 50ksi min(345Mpa min)
Yield Strength; 16ksi min(110Mpa min)
Elongation; 50% min

Product Details:

ASTM B314 Gr 2117 Aluminum Rod, is one of the leading manufacturers & suppliers of ASTM B314 Gr 2117 Aluminum Rod.

ASTM B314 Gr 2117 Chemical Composition
Aluminium; Bal
Chromium; 0.1max
Copper; 2.2-3.0
Iron; 0.7max
Magnesium; 0.2-0.5
Manganese; 0.2max
Silicon; 0.8max
Zinc; 0.25max

ASTM B314 Gr 2117 Mechanical Properties
Tensile Strength; 296Mpa, 43000psi
Yield Strength; 165Mpa, 24000psi
Elongation; 27%
Hardness, Brinell; 70

Product Details:

ASTM B316 Gr 1100 Aluminum, has very good machinability with excellent forming characteristics. It is used for chemical storage, processing equipment, kitchen utensils etc.

ASTM B316 Gr 1100 Chemical Composition
Aluminium; 99min
Copper; 0.05-0.20
Manganese; 0.05max
Silicon+Iron; 0.95max
Zinc; 0.1max

ASTM B316 Gr 1100 Mechanical Properties
Tensile Strength(Mpa); 110
Yield Strength(Mpa); 105
Elongation; 12%

Product Details:

ASTM B316 Gr 2017 Aluminum, is a heat treatable alloy of intermediate strength & good ductility. It is used to manufacture screw machine products & fittings, gauges, coat hangers etc.

ASTM B316 Gr 2017 Chemical Composition

• Aluminum; bal
• Chromium; 0.1max
• Copper; 3.5-4.5
• Iron; 0.7max
• Mangnesium; 0.4-0.8
• Manganese; 0.4-1.0
• Silicon; 0.8max
• Titanium+Zinc; 0.2max
• Zinc; 0.25max

ASTM B316 Gr 2017 Mechanical Properties
Tensile Strength; 179Mpa, 26000psi
Yield Strength; 69Mpa, 10000psi
Elongation; 22%

Product Details:

ASTM B316 Gr 2024 Aluminum Rod, is known as "aircraft alloy" in machining rod. It is one of the most poplular alloy for heading & roll threading applications. It has high strength & excellent fatigue resistance. It is commonly used in aircraft structural components, truck wheels & medical instruments.

ASTM B316 Gr 2024 Chemical Composition

• Silicon; 0.50max
• Iron; 0.50max
• Copper; 3.80-4.90
• Manganese; 1.20-1.80
• Magnesium; 0.30-0.90
• Chromium; 0.10max
• Zinc; 0.25max
• Titanium; 0.15max

ASTM B316 Gr 2024 Mechanical Properties
Tensile Strength; 68ksi, 469Mpa
Yield Strength; 47ksi, 324Mpa
Elongation; 19%
Hardness Brinell; 120

Product Details:

ASTM B316 Gr 2117 Aluminum, has the primary consistent of copper & is mainly used where medium strength is required. 

Chemical Composition
Aluminium; 94.3-97.6
Copper; 2.2-3.0
Silicon; 0.80max
Iron; 0.70max
Zinc; 0.25max
Magnesium; 0.20-0.50
Manganese; 0.20max
Chromium; 0.10max

Mechanical Properties 
Tensile Strength; 296Mpa, 43000psi
Yield Strength; 165Mpa, 24000psi
Elongation; 27%
Hardness, Brinell; 70

Product Details:

ASTM B316 Gr 2117 Aluminum, is mainly used to manufacture a variety of mechanical fasteners & rivets. It has very good workability for forming either cold or hot.

ASTM B316 Gr 2117 Chemical Composition

• Aluminium; 94.3-97.6
• Copper; 2.2-3.0
• Silicon; 0.80max
• Iron; 0.70max
• Zinc; 0.25max
• Magnesium; 0.20-0.50
• Manganese; 0.20max
• Chromium; 0.10max

ASTM B316 Gr 2117 Mechanical Properties
Tensile Strength; 296Mpa, 43000psi
Yield Strength; 165Mpa, 24000psi
Elongation; 27%
Hardness, Brinell; 70

Product Details:

Aesteiron Steels Pvt Ltd, is one of the leading suppliers of ASTM B316 Gr 2119 Aluminum Rod.

ASTM B316 Gr 2119 Chemical Composition
Chroimum; 0.15-0.35
Copper; 0.1max
Magnesium; 2.2-2.8
Manganese; 0.1max
Silicon+Iron; 0.14max
Zinc; 0.1max

Product Details:

ASTM B316 Gr 3003 Aluminum, can be cold worked using all conventional techniques. It can be hardened by cold working. It is used to manufacture gas line, storage tanks, pressure vessels, cooking utensils & heat exchangers etc.

ASTM B163 Monel 400 Chemical Composition
Cobalt; 0.05-0.20
Hydrogen; 0.70max
Magnesium; 1.00-1.50
Silicon+Iron; 0.60max
Zirconium; 0.10max
Aluminium; Bal

ASTM B163 Monel 400 Mechanical Properties
Tensile Strength; 95-135Mpa
Proof Stress; 35 Min Mpa
Hardness Brinell; 28 HB

Product Details:

ASTM B316 Gr 5005 Aluminum, has medium strength, good weldability & corrosion resistance in marine atmosphere. It also has the low density & excellent thermal conductivity common to all aluminium alloys.

ASTM B316 Gr 5005 Chemical Composition

• Aluminium; Bal
• Magnesium; 0.50-1.10
• Silicon; 0.30max
• Iron; 0.07max
• Copper; 0.20max
• Manganese; 0.20max
• Chromium; 0.10max
• Zinc; 0.25max

ASTM B316 Gr 5005 Mechanical Properties
Tensile Strength; 145-185Mpa
Proof Stress; 110 Min Mpa
Hardness Brinell; 47 HB

Product Details:

ASTM B316 Gr 5052 Aluminum, is a non heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics & good corrosion resistance, including resistance to salt water.

ASTM B316 Gr 5052 Chemical Composition
Chromium; 0.15-0.35
Copper; 0.1max
Magnesium; 2.2-2.8
Manganese; 0.1max
Silicon+Iron; 0.45max
Zinc; 0.1max
Aluminium; Bal

ASTM B316 Gr 5052 Mechanical Properties
Tensile Strength; 210-260Mpa
Proof Stress; 130 Min Mpa
Hardness Brinell; 61HB

Product Details:

ASTM B316 Gr 5056 Aluminum, has strong corrosion resistance charcteristics & high electrical conductivity. It is used in cable sheathings, rivets for magnesium & zippers.

Chemical Composition
Aluminium; Bal
Silicon; 0.3max
Iron; 0.4max
Copper; 0.10max
Manganese; 0.05-0.20
Chromium; 0.05-0.20
Magnesium; 4.50-5.60
Zinc; 0.10max

Mechanical Properties
Tensile Strength; 414Mpa, 60000psi
Yield Strength; 345Mpa, 50000psi
Hardness, Brinell: 100
Elongtion; 15%

Product Details:

ASTM B316 Gr 6061 Aluminum, is one of the most extensively used aluminium alloys. It is a versatile heat treatable extruded alloy with medium to high strength capabilities.

Chemical Composition
Aluminium; Bal
Magnesium; 0.8-1.2
Silicon; 0.4-0.8
Iron; 0.7max
Copper; 0.15-0.40
Zinc; 0.25max
Titanium; 0.15max
Manganese; 0.15max
Chromium; 0.04-0.35

Mechanical Properties
Tensile Strength(Mpa); 110-152
0.2% Proof Stress(Mpa); 65-110
Brinell Hardness; 30-33
Elongation 50mm dia(%); 14-16%

Product Details:

ASTM B316 Gr 7050 Aluminum, is an aerospace grade of aluminium combining high strength, stress corrosion cracking resistance & toughness.

ASTM B316 Gr 7050 Chemical Composition
Aluminium; 87.3-90.3
Zirconium; 0.08-0.15
Silicon; 0.12max
Iron; 0.15max
Copper; 2.0-2.6
Manganese; 0.10max
Magnesium; 1.9-2.6
Zinc; 0.04max
Chromium; 0.04max
Zinc; 5.7-6.7
Titanium; 0.06max

Product Details:

ASTM B316 Gr 7050 Aluminum, provides better corrosion resistance characteristics. It is commonly used to manufacture aircraft & other structure.

ASTM B316 Gr 7050 Chemical Composition

• Silicon; 0.12max
• Iron; 0.15max
• Copper; 2.0-2.6
• Manganese; 0.1max
• Magnesium; 1.9-2.6
• Chromium; 0.04max
• Zinc; 5.7-6.7
• Titanium; 0.06max

ASTM B316 Gr 7050 Mechanical Properties
Tensile Strength; 83-73ksi
Yield Strength; 73-63
Elongation; 13-11%

Product Details:

ASTM B366 Nickel 201, is a commercially pure wrought nickel, with good mechanical properties & an excellent resistance to many corrosives. It is mainly used for food processing equipment, chemical shipping drums, caustic handling equipment & piping, electronic parts etc.

ASTM B366 Nickel 201 Chemical Composition
Carbon; 0.02max
Manganese; 0.35max
Copper; 0.25max
Silicon; 0.35max
Sulfur; 0.01max
Iron; 0.40max
Nickel; 99.0min

ASTM B366 Nickel 201 Mechanical Properties
Tensile Strength; 55-75ksi, 380-520Mpa
0.2% Offset Yield Strength; 15-30ksi, 105-210Mpa
Elongation in 2"; 55-40%

Product Details:

ASTM B730 Nickel 201, is used for food processing equipment, marine & offshore engineering, salt production & caustic handing equipment.

ASTM B730 Nickel 201 Chemical Composition
Nickel; 99.0min
Iron; 0.40max
Copper; 0.25max
Carbon; 0.15max
Manganese; 0.35max
Sulfur; 0.01max
Silicon; 0.35max

ASTM B730 Nickel 201 Mechanical Properties
Tensile Strength; 55-75ksi
0.2% Yield Strength; 12-30ksi
Elongation; 40-60%
Hardness; 70max

Product Details:

ASTM F3 Nickel 233, is a commercially pure wrought nickel alloy that exhibits excellent corrosion resistance & high electrical & thermal conductivities.

ASTM F3 Nickel 233 Chemical Composition
Carbon; 0.1max
Manganese; 0.3max
Magnesium; 0.01-0.10
Silicon; 0.1max
Iron; 0.1max
Copper; 0.1max
Sulfur; 0.008max
Titanium; 0.005max
Nickel; Bal

ASTM F3 Nickel 233 Mechanical Properties
Tensile Strength; 650-880Mpa, 94275-127633psi
Yield Strength; 350-550Mpa, 50763-79771psi
Elongation; 8-25%