Aluminum Tube

Product Details:

ASTM B221 Gr 6066 Aluminum has good corrosion resistance. Its strength can also be increased when it exposed to subzero temperatures.

Chemical Composition

• Aluminum; 95.7max
• Silicon; 1.40max
• Manganese; 1.10max
• Copper; 1.00max
• Manganese; 0.80max

Mechanical Properties

• Tensile Strength(Mpa)psi; (150)21755
• Yield Strength(Mpa)psi; (83)12038
• Hardness, Brinell; 43

Product Details:

ASTM B209 Gr 1050 Aluminum provides excellent corrosion resistance, high ductiliy & highly reflective finish.

ASTM B209 Gr 1050 Chemical Composition

• Copper; 0.05
• Maganesium; 0.05
• Silicon; 0.25
• Iron; 0.4
• Manganese; 0.05
• Zinc; 0.07max
• Titanium; 0.05max
• Aluminium; Bal

ASTM B209 Gr 1050 Mechanical Properties
Proof Stress; 85min(Mpa)
Tensile Strength; 105-145(Mpa)
Hardness Brinell; 34HB
Elongation; 12%min

Product Details:

ASTM B210 Gr 1060 Aluminum, is a low strength & pure aluminium with good corrosion resistance characteristics. It is widely used in the manufacture of railroad tank cars & chemical equipment.

Chemical Composition

• Aluminium; 99.60min

Mechanical Properties

• Elastic Modulus; 70-80Mpa, 10152-11603ksi
• Poisson's ratio; 0.33

Product Details:

ASTM B210 Gr 1100 Aluminum, is commercially pure aluminium with excellent forming characteristic. It is commonly used in heat exchanger fins, cooking utensils, giftware, rivets & reflectors.

ASTM B210 Gr 1100 Chemical Composition

• Aluminium; 99min
• Copper; 0.05-0.20
• Manganese; 0.05max
• Silicon+Iron; 0.95max
• Zinc; 0.1max

Product Details:

ASTM B210 Gr 2011 Aluminum, provides strong corrosion resistance. It is considered as good low temperature alloys as their strength increases when exposed to subzero temperature & they lose some of the strength when exposed to high temperature.

ASTM B210 Gr 2011 Chemical Composition

• Aluminium; 93.7
• Copper; 5.5
• Bismuth; 0.4
• Lead; 0.4

ASTM B210 Gr 2011 Mechanical Properties
Elastic modulus; 70-80Mpa; 10152-11603ksi
Poisson ratio; 0.33

Product Details:

ASTM B210 Gr 2014 Aluminum, provides strong corrosion resistance characteristics & high electrical conductivity. The strength of these alloy increase at subzero temperature & strength is lost when these alloys are exposed to high temperature.

ASTM B210 Gr 2014 Chemical Composition

• Aluminium; 93.5
• Copper; 4.4
• Silicon; 0.8
• Magnesium; 0.5
• Chromium; 0.1
• Manganese; 0.6

ASTM B210 Gr 2014 Mechanical Properties
Elastic modulus; 70-80Mpa, 10152-11603ksi
Poisson ratio; 0.33

Product Details:

ASTM B210 Gr 2024 Aluminum, is commonly used in the manufacture of truck wheels, aircraft structures, screw machine products, scientific instruments etc.

ASTM B210 Gr 2024 Chemical Composition
Aluminium; Bal
Chromium; 0.1max
Copper; 3.8-4.9
Iron; 0.5max
Magnesium; 1.2-1.8
Manganese; 0.3-0.9
Silicon; 0.50max
Zinc; 0.25max

Product Details:

ASTM B210 Gr 3003 Aluminum, is commonly used in chemical equipment, ductwork & in general sheet metal work.It is also used to manufacture cooking utensile, pressure vessels, garage doors, heat exchangers, refrigerator panels & storage tanks.

ASTM B210 Gr 3003 Chemical Composition

• Aluminium; Bal
• Copper; 0.05-0.20
• Iron; 0.7max
• Manganese; 1.0-1.5
• Silicon; 0.6max
• Zinc; 0.1max

Product Details:

ASTM B210 Gr 5005 Aluminum, has the same high resistance to general corrosion as other non heat treatable aluminium alloys. Its applications are architectural, high strength foil & general sheet metal work.

ASTM B210 Gr 5005 Chemical Composition

• Aluminium; Bal
• Magnesium; 0.50-1.10
• Silicon; 0.30max
• Iron; 0.07max
• Copper; 0.20max
• Manganese; 0.20max
• Chromium; 0.10max
• Zinc; 0.25max

ASTM B210 Gr 5005 Mechanical Properties

• 0.2% Proof Stress, Mpa: 35min
• Tensile Strength, Mpa: 105-145
• Elongation; 12-22%

Product Details:

ASTM B210 Gr 5050 Aluminum, has excellent corrosion resistance. It is a wrought type alloy. It has excellent workability & is non heat treatble alloy.

ASTM B210 Gr 5050 Chemical Composition
Aluminum; 98.6max
Magnesium; 1.4max

ASTM B210 Gr 5050 Mechanical Properties
Elastic Modulus; 70-80Mpa, 10152-11603ksi
Poissons ratio; 0.33

Product Details:

ASTM B210 Gr 5052 Aluminum has good corrosion resistance to seawater, marine & industrial atmosphere. It also has very good weldability & good cold formability. Its applications are chemical industry, pressure vessels, irrigation & architectural paneling.

ASTM B210 Gr 5052 Chemical Composition

• Manganese; 0.10max
• Iron; 0.40max
• Copper; 0.10max
• Magnesium; 2.20-2.80
• Silicon; 0.25max
• Zinc; 0.10max
• Chromium; 0.15-0.35
• Aluminium; Bal

ASTM B210 Gr 5052 Mechanical Properties
Tensile Strength, Mpa: 210-260
Proof Stress, Mpa: 130min
Hardness Brinell; 61HB

Product Details:

ASTM B210 Gr 5083 Aluminum Tube is known for its exceptional performance in extreme environments.

ASTM B210 Gr 5083 Chemical Composition

• Silicon; 0.40max
• Iron; 0.40max
• Copper; 0.10max
• Manganese; 0.4-1.0
• Magnesium; 4.0-9.0
• Zinc; 0.25max
• Titanium; 0.15max
• Chromium; 0.05-0.25
• Aluminum; Bal

ASTM B210 Gr 5083 Mechanical Properties

• Proof Stress; 125Mpa,min
• Tensile Strength; 275-350Mpa
• Hardness Brinell; 75HB

Product Details:

ASTM B210 Gr 5086 Aluminum Tube has higher strength than 5052 & 5083 & its mechanical properties vary significantly with hardening & temperature. Its applications are tank cars, shipyard, patrol & work boat hulls.

ASTM B210 Gr 5086 Chemical Composition

• Silicon; 0.4max
• Iron; 0.5max
• Copper; 0.1max
• Manganese; 0.20-0.70
• Magnesium; 3.5-4.5
• Chromium; 0.05-0.25max
• Zinc; 0.25max
• Titanium; 0.15max

ASTM B210 Gr 5086 Mechanical Properties

• Tensile Strength(ksi); 44
• Yield Strength(ksi); 14
• Elongation; 16%

Product Details:

ASTM B210 Gr 5154 Aluminum has strong corrosion resistance. It is a wrought alloy.

ASTM B210 Gr 5154 Chemical Composition

• Aluminium; 96.2
• Magnesium; 3.5
• Chromium; 0.25

ASTM B210 Gr 5154 Mechanical Properties

• Elastic Modulus; 70-80Mpa, 10152-11603ksi
• Poisson's ration; 0.33

Product Details:

ASTM B210 Gr 5456 Aluminum has good strength & is useful for structural purpose because of its weldable characteristic.

ASTM B210 Gr 5456 Chemical Composition

• Aluminium; 93.9
• Magnesium; 5.1
• Chromium; 0.12
• Manganese; 0.8

ASTM B210 Gr 5456 Mechanical Properties

• Elastic modulus; 70-80Mpa, 10152-11603ksi
• Poisson's ratio; 0.33

Product Details:

ASTM B210 Gr 6061 Aluminum Tube is one of the most extensively used of the 6000 series aluminium alloys. It is a versatile heat treatable extruded alloy with medium to high strength capabilities.

ASTM B210 Gr 6061 Chemical Composition

• Aluminum; Bal
• Magnesium; 0.8-1.2
• Silicon; 0.4-0.8
• Iron; 0.7max
• Copper; 0.15-0.40
• Zinc; 0.25max
• Titanium; 0.15max
• Manganese; 0.15max
• Chromium; 0.04-0.35

ASTM B210 Gr 6061 Mechanical Properties

• Tensile Strength(Mpa); 110-152
• 0.2% Proof Strength(Mpa); 65-110
• Brinell Hardness; 30-33
• Elongation in 50mm; 14-16%

Product Details:

ASTM B210 Gr 6063 Aluminum, has good surface finish, high corrosion resistance, it is readily suited to welded.

ASTM B210 Gr 6063 Chemical Composition

• Silicon; 0.2-0.6
• Iron; 0.35max
• Copper; 0.1max
• Manganese; 0.1max
• Magnesium; 0.1max
• Zinc; 0.1max
• Titanium; 0.1max
• Chromium; 0.1max
• Aluminum; Bal

ASTM B210 Gr 6063 Mechanical Properties

• Tensile Strength(Mpa); 130max
• Elongation; 16%min
• Hardness; 25HB

Product Details:

6262 Aluminum Tube is a free machining alloy that offers users outstanding mechanical strength & good resistance to corrosion

ASTM B210 Gr 6262 Chemical Composition

• Aluminum; Bal
• Magnesium; 0.8-1.2
• Copper; 0.4-1.4
• Chromium; 0.20max
• Manganese; 0.15max
• Zinc; 0.25max
• Titanium; 0.15max
• Lead; 0.7max
• Bismuth; 0.7max
• Iron; 0.7max

Product Details:

ASTM B210 Gr 7075 Aluminum is one of the highest strength aluminum alloys. It is often used where parts are highly stressed.

ASTM B210 Gr 7075 Chemical Composition

• Silicon; 0.40max
• Iron; 0.50max
• Copper; 1.20-2.00
• Manganese; 0.30max
• Magnesium; 2.10-2.90
• Chromium; 0.18-0.28
• Zinc; 5.10-6.10
• Titanium; 0.20max

Product Details:

ASTM B221 Gr 1062 Aluminum has strong corrosion resistance. At zero temperature, their strength increases, thus making them a useful low temperature alloy. Their strength decreases if they are subjected to very high temperatures.

ASTM B221 Gr 1062 Chemical Composition

• Aluminum; 90
• Zinc; 5.6
• Magnesium; 2.5
• Copper; 1.6
• Chromium; 0.23

ASTM B221 Gr 1062 Mechanical Properties

• Tensile Strength(Mpa)psi; (220)31909
• Yield Strength(Mpa)psi; (95)13779
• Elongation; 17%
• Hardness; 60

Product Details:

ASTM B221 Gr 1100 Aluminum is among the softest aluminum alloys & therefore is not used for high strength or high pressure applications.

ASTM B221 Gr 1100 Chemical Composition

• Aluminum; 99min
• Copper; 0.05-0.20
• Manganese; 0.05max
• Silicon+Iron; 0.95max
• Zinc; 0.1max

Product Details:

ASTM B221 Gr 2014 Aluminum Tube is a copper based alloy with very high strength together with excellent machining characteristics. It is commonly used in many aerospace structural applications due to its high strength.

ASTM B221 Gr 2014 Chemical Composition

• Aluminum; Rem
• Silicon; 0.50-1.20
• Iron; 0.7max
• Copper; 3.9-5.0
• Manganese; 0.4-1.2
• Chromium; 0.10max
• Magnesium; 0.2-0.8
• Zinc; 0.25max
• Titanium; 0.15max

Product Details:

ASTM B221 Gr 2024 Aluminum tube is a copper alloyed aluminum product that is primarily used in aircraft applications where hig strength & good fatigue resistance is required.

ASTM B221 Gr 2024 Chemical Composition

• Silicon; 0.50max
• Iron; 0.50max
• Copper; 3.80-4.90
• Manganese; 0.30-0.90
• Magnesium; 1.2-1.8
• Chromium; 0.10max
• Zinc; 0.25max
• Titanium; 0.15max

ASTM B221 Gr 2024 Mechanical Properties

• Tensile Strength(ksi)Mpa; (27)186
• Yield Strength(ksi)Mpa; (11)76
• Elongation; 22%
• Hardness Brinell; 47

Product Details:

ASTM B221 Gr 2219 Aluminum, is an age hardenable alloy is produced with a copper additive. It is well known for its excellent strength & it is used for numerous high temperature applications. It is a suitable alloy for many metalworking process including machining, heat treatment, cold working etc.

ASTM B221 Gr 2219 Chemical Composition

• Copper; 5.8-6.8
• Manganese; 0.20-0.40
• Magnesium; 0.02%
• Iron; 0.30%
• Silicon; 0.20%
• Zinc; 0.10%
• Zirconium; 0.10-0.25%
• Titanium; 0.2-10%

Product Details:

ASTM B221 Gr 3003 Aluminum Tube is a manganese alloyed aluminum product that is primarily used for heat exchangers & condensers in chemical equipment & pressure vessels. It has good corrosion resistance, workability & weldability characteristics.

ASTM B221 Gr 3003 Chemical Composition

• Silicon; 0.60max
• Iron; 0.70max
• Copper; 0.05-0.20
• Manganese; 1.0-1.5
• Zinc; 0.10max

ASTM B221 Gr 3003 Mechanical Properties

• Tensile Strength(ksi)Mpa; (16)110
• Yield Strength(ksi)Mpa; (6)40
• Elongation; 30%
• Hardness Brinell; 28

Product Details:

ASTM B221 Gr 5052 Aluminum Tube, is a magnesium alloyed aluminum primarily used in hydraulic tube & appliance applications. It also provides good corrosion resistance & weldability.

ASTM B221 Gr 5052 Chemical Composition

• Silicon; 0.25max
• Iron; 0.40max
• Copper; 0.10max
• Manganese; 0.10max
• Magnesium; 2.20-2.80
• Chromium; 0.15-0.35
• Zinc; 0.10max

ASTM B221 Gr 5052 Mechanical Properties

• Ultimate Tensile Strength; 28ksi, 195Mpa
• Yield Strength; 13ksi, 90Mpa
• Elongation; 25%

Product Details:

ASTM B221 Gr 5083 Aluminum has good weldability characteristics for fabricating vessels. It is primarily used in marine industry due to its excellent corrosion resistance.

ASTM B221 Gr 5083 Chemical Composition

• Silicon; 0.40max
• Iron; 0.40max
• Copper; 0.10max
• Manganese; 0.40-1.0
• Magnesium; 4.0-4.9
• Chromium; 0.05-0.25
• Zinc; 0.25max
• Titanium; 0.15max

ASTM B221 Gr 5083 Mechanical Properties

• Ultimate Tensile Strength; 45ksi, 310Mpa
• Yield Strength; 20ksi, 125Mpa
• Elongation; 14%

Product Details:

ASTM B221 Gr 5154 Aluminum, is non heat treatable alloy. It has strong corrosion resistance. It can be enhanced at subzero temperatures, making them ideal low temperature alloys.

ASTM B221 Gr 5154 Chemical Composition

• Aluminum; 96.2max
• Magnesium; 3.5max
• Chromium; 0.25max

ASTM B221 Gr 5154 Mechanical Properties

• Elastic modulus; 70-80Mpa, 10152-11603ksi
• Poisson ratio; 0.33

Product Details:

We are involved in offering a wide range of ASTM B221 Gr 5186 Aluminum Tube.

ASTM B221 Gr 5186 Chemical Composition

• Iron; 0.35max
• Silicon; 0.10max
• Copper; 0.20max
• Manganese; 0.2-0.5
• Magnesium; 4.0-5.0
• Zinc; 0.25max
• Titanium; 0.12max

ASTM B221 Gr 5186 Mechanical Properties

• Yield Strength(Mpa); 135max
• Tensile Strength(Mpa); 290max
• Elongation; 22%
• Hardness(Brinell); 55

Product Details:

ASTM B221 Gr 5454 Aluminum is a non-heat treatable alloy aluminum & magnesium. It is commonly used to manufacture welded structures, pressure vessels & in marine services.

ASTM B221 Gr 5454 Chemical Composition

• Aluminum; Bal
• Chromium; 0.05-0.20
• Copper; 0.1max
• Magnesium; 2.4-3.0
• Manganese; 0.5-1.0
• Titanium; 0.2max
• Zinc; 0.25max

Product Details:

ASTM B221 Gr 5456 Aluminum is an alloy of aluminum & magnesium with good strength. It is good for structural use because of its good weldability.

ASTM B221 Gr 5456 Chemical Composition

• Aluminum; Bal
• Chromium; 0.05-0.20
• Copper; 0.1max
• Iron; 0.4max
• Magnesium; 4.7-5.5
• Manganese; 0.5-1.0
• Silicon; 0.25max
• Titanium; 0.2max
• Zinc; 0.25max

Product Details:

ASTM B221 Gr 6005 Aluminum Tube has properties between those of alloy 6061 & 6082 & can be used interchangeably with these alloys but 6005 has better extrusion characteristics.

ASTM B221 Gr 6005 Chemical Composition

• Silicon; 0.5-0.9
• Iron; 0.35max
• Copper; 0.3max
• Manganese; 0.5max
• Magnesium; 0.4-0.7
• Zinc; 0.2max
• Titanium; 0.1max
• Chromium; 0.3max
• Aluminium; Bal

ASTM B221 Gr 6005 Mechanical Properties

• Proof Stress; 225(Mpa)min
• Tensile Strength; 270(Mpa)min
• Elongation; 10%min
• Hardness Brinell; 90HB

Product Details:

We provide premium quality of ASTM B221 Gr 6060 Aluminum Tube.

ASTM B221 Gr 6060 Chemical Composition

• Chromium; 0.05max
• Manganese; 0.10max
• Magnesium; 0.35-0.60
• Silicon; 0.30-0.60
• Copper; 0.10max
• Zinc; 0.15max
• Titanium; 0.10max
• Iron; 0.10-0.30
• Aluminium; Bal

ASTM B221 Gr 6060 Mechanical Properties

• Tensile Strength(Mpa); 160min
• Elongation; 6min%
• Hardness Brinell; 60

Product Details:

Aesteiron Steels Pvt Ltd, provides premium quality ASTM B221 Gr 6061 Aluminum Tube.

ASTM B221 Gr 6061 Chemical Composition

• Silicon; 0.40-0.80
• Iron; 0.70max
• Copper; 0.15-0.40
• Manganese; 0.15max
• Magnesium; 0.80-1.20
• Chromium; 0.04-0.35
• Zirconium; 0.25max
• Titanium; 0.15max

ASTM B221 Gr 6061 Mechanical Properties

• Tensile Strength(ksi)Mpa; (45)310
• Yield Strength(ksi)Mpa; (40)276
• Elongation; 12%

Product Details:

ASTM B221 Gr 6063 Aluminum it is generally considered to be an extrusion alloy that is heat treatable for strengthening. It is used for manufacturing furniture, stair rails, windows etc.

ASTM B221 Gr 6063 Chemical Composition

• Aluminum; Bal
• Chromium; 0.1max
• Copper; 0.1max
• Iron; 0.35max
• Magnesium; 0.45-0.90
• Manganese; 0.1max
• Silicon; 0.2-0.6
• Titanium; 0.1max
• Zinc; 0.1max

Product Details:

ASTM B221 Gr 6105 Aluminum is used in many industries & it is an excellent conductor of heat & electricity. Its a wrought alloy with good corrosion resistance & medium strength.

ASTM B221 Gr 6105 Chemical Composition

• Aluminum; Rem
• Silicon; 0.6-1.0
• Manganese; 0.45-0.80
• Chromium; 0.10max
• Copper; 0.10max
• Manganese; 0.10max
• Zinc; 0.10max
• Titanium; 0.10max
• Iron; 0.35max

Product Details:

ASTM B221 Gr 6262 Aluminum Tube is a free machining alloy that offers users outstanding mechanical strength & good corrosion resistance.

ASTM B221 Gr 6262 Chemical Composition

• Aluminium; bal
• Magnesium; 0.8-1.2
• Copper; 0.4-1.4
• Chromium; 0.20max
• Manganese; 0.15max
• Zinc; 0.25max
• Titanium; 0.15max
• Lead; 0.7max
• Bismuth; 0.7max
• Iron; 0.7max

Product Details:

Aesteiron Steels Pvt Ltd, is the suppliers of high quality ASTM B221 Gr 6351 Aluminum Tube.

ASTM B221 Gr 6351 Chemical Composition

• Aluminum; 97.8
• Silicon; 1.00
• Manganese; 0.6
• Magnesium; 0.6

ASTM B221 Gr 6351 Mechanical Properties

• Tensile Strength(Mpa)psi; (250)36260
• Yield Strength(Mpa)psi; (150)21756
• Elongation; 20%
• Hardness; 95

Product Details:

ASTM B221 Gr 6463 Aluminum, strength can be lost when they are exposed to high temperatures. It also has high corrosion resistance.

ASTM B221 Gr 6463 Chemical Composition

• Aluminum; 98.9
• Mangnesium; 0.70
• Silicon; 0.40

ASTM B221 Gr 6463 Mechanical Properties

• Tensile Strength(Mpa)psi; (150)21756
• Yield Strength(Mpa)psi; (90)10354
• Elongation; 20%
• Hardness; 42